Rita M. F. Cardoso

Abstract Given the growing scarcity of water and the continuous increase in emerging pollutants detected in water bodies, there is an imperative need to develop new, more effective, and sustainable treatments for wastewater. Advanced oxidation processes (AOPs) are considered a competitive technology for water treatment. Specifically, ozonation has received notable attention as a promising approach for degrading organic pollutants in wastewater. However, different groups of pollutants are hardly degradable via single ozonation. With continuous development, it has been shown that using engineered nanomaterials as nanocatalysts in catalytic ozonation can increase efficiency by turning this process into a low-selective AOP for pollutant degradation. Nanocatalysts promote ozone decomposition and form active free radicals responsible for increasing the degradation and mineralization of pollutants. This work reviews the performances of different nanomaterials as homogeneous and heterogeneous nanocatalysts in catalytic ozonation. This review focuses on applying metal- and carbon-based engineered nanomaterials as nanocatalysts in catalytic ozonation and on identifying the main future directions for using this type of AOP toward wastewater treatment.

Abstract UV-based advanced oxidation processes (AOPs) (UV/H2O2 and UV/S2O82-) with a titanium(IV)-doped carbon dot, TiP-CD, as a catalyst were developed for the decomposition of Remazol Brilliant Blue R (Reactive Blue 19), an anthraquinone textile dye (at T = 25 degrees C and pH = 7). The Ti-CD, with marked catalytic UV properties, was successfully synthesized by the one-pot hydrothermal procedure, using L-cysteine as carbon precursor, ethylenediamine as nitrogen source, PEG (polyethylene glycol) as a capping agent, and titanium(IV) isopropoxide (precursor of TiO2 doping). Contrary to azo dyes (methyl orange, orange II sodium salt, and reactive black 5), which achieved complete degradation in a time interval less than 30 min in the developed AOP systems (UV/H2O2, UV/S2O82-, and UV/TiO2), the RBB-R showed relatively low degradation rates and low discoloration rate constants. In the presence of the catalyzer, the reaction rate significantly increased, and the pseudo-first-order rate constants for the RBB-R discoloration were UV/3.0 mM H2O2/TIP-CD-0.0330 min(-1) and UV/1.02 mM S2O82-/TIP-CD-0.0345 min(-1).

Abstract A catalytic ozonation advanced oxidation process (AOP) with a copper(II)-doped carbon dot as catalyst, Cu-CD (using L-cysteine and polyethylene glycol (PEG) as precursors and passivation agents), was developed for textile wastewater treatment (T = 25 degrees C and pH = 7). Four dyes were analyzed-Methyl Orange (MO), Orange II sodium salt (O-II), Reactive Black 5 (RB-5) and Remazol Brilliant Blue R (RBB-R), as well as a real effluent from the dying and printing industry. The Cu-CD, with marked catalytic ozonation properties, was successfully synthesized by one-pot hydrothermal procedure with a size of 4.0 nm, a charge of -3.7 mV and a fluorescent quantum yield of 31%. The discoloration of the aqueous dye solutions followed an apparent first-order kinetics with the following rate constants (k(ap) in min(-1)): MO, 0.210; O-II, 0.133; RB-5, 0.177; RBB-R, 0.086. In the presence of Cu-CD, the following apparent first-order rate constants were obtained (k(ap)(C) in min(-1)) with the corresponding increase in the rate constant without catalyst (%Inc): MO, 1.184 (464%); O-II, 1.002 (653%); RB-5, 0.709 (301%); RBB-R, 0.230 (167%). The presence of sodium chloride (at a concentration of 50 g/L) resulted in a marked increase of the discoloration rate of the dye solution due to generation of other radicals, such as chlorine and chlorine oxide, resulting from the reaction of ozone and chloride. Taking into consideration that the real textile effluent under research has a high carbonate concentration (>356 mg/L), which inhibits ozone decomposition, the discoloration first-order rate constants without and with Cu-CD (k(ap) = 0.0097 min(-1) and k(ap)(C) = 0.012 min(-1) (%Inc = 24%), respectively) were relatively small. Apparently, the Cu-CD, the surface of which is covered by a soft and highly hydrated caramelized PEG coating, accelerates the ozone decomposition and dye adsorption, increasing its degradation.

Abstract Water quality management will be a priority issue in the near future. Indeed, due to scarcity and/or contamination of the water, regulatory frameworks will be increasingly strict to reduce environmental impacts of wastewater and to allow water to be reused. Moreover, drinking water quality standards must be improved in order to account for the emerging pollutants that are being detected in tap water. These tasks can only be achieved if new improved and sustainable water treatment technologies are developed. Nanomaterials are improving the ongoing research on advanced oxidation processes (AOPs). This work reviews the most important AOPs, namely: persulfate, chlorine and NH2Cl based processes, UV/H2O2, Fenton processes, ozone, and heterogeneous photocatalytic processes. A critical review of the current coupling of nanomaterials to some of these AOPs is presented. Besides the active role of the nanomaterials in the degradation of water contaminants/pollutants in the AOPs, the relevance of their adsorbent/absorbent function in these processes is also discussed.